EFFECT OF ZNO NANOPARTICLES ON PROPERTIES OF NANOCOMPOSITE COATING BASED ON ACRYLIC POLYMER EMULSION AND GRAPHENE OXIDE

Phi Hung Dao, Trinh Van Thanh, Nguyen Anh Hiep, Nguyen Thien Vuong, Mac Van Phuc, Dang Thi My Linh

Abstract


Effect of ZnO nanoparticles on nanocomposite coatings based on R4152 and graphene oxide (GO) was studied.In presence of 2%wt. ZnO nanoparticle, abrasion resistance of coating increased by nearly 25% (from 75 to 92.9 L/mil) and temperature decomposition raised by 18oC. SEM images showed that nano ZnO can disperse homogenously in polymer matrix in presence of GO. Hence, photocatalytic activity of R4152/GO/ZnO nanocomposite coating was higher than that of R4152/ZnO nanocomposite coating. After 14 hours UV exposure, R4152/GO/ZnO nanocomposite coating can degrade over 80% methylene blue coated on its surface while 60% methylene blue was degraded by R4152/ZnO coatings.


Keywords


acrylic polymer emulsion, graphene oxide, ZnO nanoparticle, photocatalytic activity, thermal stability, abrasion resistance



DOI: https://doi.org/10.15625/2525-2518/59/3/15751 Display counter: Abstract : 0 views.

Refbacks

  • There are currently no refbacks.


Bioteknologi Agrikultur

Index: Google Scholar; Crossref; VCGate; Asean Citation Index

Published by Vietnam Academy of Science and Technology